E6013 is a mild steel welding rod with rutile type coating.
AWS A5.1 E6013
BS EN IS0 2560-B-E 43 13 A
CSA W48-06 E4313
JIS Z3211 D4313
GB/T5117 E4313
Type of Covering: High Titania, Potassium
Welding Position: F,H,HF,OH,V
Type of Current: AC, DCEP or DCEN
Features & Applications
E6013 is a mild steel welding rod with rutile type coating. It welds on AC & DC and widely used in ordinary tensile strength mild steel structures. Especially suitable for intermittent welding to sheet steel and small work pieces as well as cosmetic welding with smooth and shiny appearance.
Rutile type E6013 – Grade 4 Coating contains reduction titanium & natural rutile
Chemical Composition of Deposited Metal(%)
| C | Mn | Si | S | P | Ni | Cr | Mo | V | |
| Standard | ≤0.20 | ≤1.20 | ≤1.00 | ≤0.035 | ≤0.040 | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
| Typical | 0.070 | 0.41 | 0.26 | 0.021 | 0.023 | 0.018 | 0.027 | 0.002 | 0.001 |
Mechanical Properties of Deposited Metal(AW)
| Yield Point Reh (Mpa) |
Tensile Strength Rm(Mpa) |
Elongation A4(%) |
Impact Value(J) | ||
| 20°C | 0°C | ||||
| Standard | ≥306 | 400-560 | ≥22 | — | ≥47 |
| Typical | 395 | 480 | 29 | 110 | 80 |
The standard of mechanical properties conforms to shipping institutions and the certificate of inspection would follow it unless the purchaser has special requirement.
X-ray radiographic inspection: Grade II
Size,Piece & Recommended Current(AC or DC⁺)
| Size(mm) | 2.5×300 | 2.5×350 | 3.2×350 | 4.0×400 | 4.0×450 | 5.0×400 | 5.0×450 | |
| Piece（5kg） | ≈303 | ≈258 | ≈157 | ≈90 | ≈80 | ≈59 | ≈52 | |
| Current(A) | F,H | 60-90 | 60-90 | 80-130 | 150-190 | 150-190 | 180-250 | 180-250 |
| V,OH | 50-80 | 50-80 | 80-110 | 130-170 | 130-170 | — | — | |
Notice: Normally the rod do not need to re-dry in case it is affected with damp seriously it should be re-baked at 150°C for 30-60 minutes before use.
All Position Welding